Heat Shrink Anode Caps are used to seal and protect the critical connection between the lead wire and anode.

It provides stress relief, moisture proofing and electrical insulation at the lead wire exit point.
It is a ideal solution to the problem of premature system failure due to corrosion causing the lead wire to come out of the anode.

Download product sheet
  • It is made from a highly cross-linked Polyolefin material
  • Black mastic coated inside the cap is designed to adhere to anode materials and wire insulation
  • Provides water tight sealing

anode cap

selection chart

Properties ValueStandard
Physical
 
Tensile strength12 N/mm² (Mpa) (min)ASTM D638
Ultimate elongation350% (min)ASTM D639
Density1,1 gm/cm²ASTM D792
Hardness45 + 10 Shore DASTM D2240
Water absorption0,2% (max)ASTM D570
CorrosionNon corrosiveASTM D2671
Thermal

Accelerated ageing120°C for 500HrsASTM D2671
Tensile strength11 N/mm² (Mpa) (min)ASTM D638
Ultimate elongation300% (min)ASTM D638
-40°C for 4HrsNo crackingASTM D2671
250°C for 30 min
No cracking or flowing
ESI 09-11
Shrink temperature125°C
IEC 216
Operating temperatureMinus 55°C to Plus 100°C
IEC 216
Electrical

Dielectric strength12 KV/mm (min)ASTM D14
Volume resistivity11 x 10¹? Ohm.cm (min)ASTM D257
Dielectric constant5 (max)ASTM D150
Products
Grouped product items
Sku Product Name

Enter the quantities you want to order / request.


Keep the quantities equal to the Order unit

Order unit
Qty
8.507800 Anode cap 82/40mm Order unit
8.507810 Anode cap 108/40mm Order unit
8.5078 Anode cap 82/40mm Order unit
8.50781 Anode cap 108/40mm Order unit
Products