FiloSlim P2662 is a cold curing two-component polyurethane resin developed for high voltage cable joints up to 10kV. This resin is composed of polyether polyols and ester polyols and has fire retardant properties.
The P2662’s moisture resistant formula is LIW classified (low voltage, insulating, water cured) according to CENELEC HD 631-1 S2 specification. The resin has been specially designed for manual filling.
The FiloSlim resin package comes with an integrated filling nipple. After mixing the resin, the package is placed on the injection valve and opened with a quarter turn. This anchors the pack to the injection valve and the cable joint can now be filled.
Once the cable joint is filled, remove the packaging with a reverse quarter turn. This simple action ensures that both the injection valve and the resin packaging are leak proof. A partially used resin pack can be used in another joint.
|Potlife (process time)|
|0.3 l at 5°C||minutes||34||IEC 60455-2|
|0.3 l at 40°C||minutes||7.5||IEC 60455-2|
|Density||g/cm³||1.2||EN ISO 1183-1|
|Impact strength||kJ/m²||33.8 (no break)||EN ISO 179|
|Hardness||Shore D||41||EN ISO 868|
|Tensile strength||MPa||8.29||EN ISO 527|
|Elongation at break||%||112||EN ISO 527|
|Curing in the presence of water - Gas volume||ml||0||IEC 60455-2|
|Volume resistivity at room temperature||Ohm||1,1x10¹⁵||IEC 60093|
|Dielectric strength at room temperature||kV/mm||>20 kV/mm||EN 60243-1|
|Temperature resistance||°C||-25 tot +120|
|Dry heat resistance: 28 days at 120°C||IEC 60455-2|
|Mass loss||%||2.89||HD 631.1 S2: 2007-12|
|Impact strength||kJ/m²||23.7||EN ISO 179|
|Wet heat resistance: 28 days at 90°C||IEC 60455-2|
|Hardness (retention/original)||%||85||EN ISO 868|
|Tensile strength (retention/original)||%||85.5||EN ISO 527|
|Elongation at break (retention/original)||%||122||EN ISO 527|
|Dielectric strength||kV/mm||18.1||EN 60243-1|